AISI 904L UNS N08904 W 1.4539
AISI 904L UNS N08904 W 1.4539 superaustenitic stainless steel is similar to 316L but with the addition of molybdenum, which gives superior resistance to localized corrosion attack (pitting and crevice corrosion).
With a PREN value of 35, it is one of the suitable solutions for applications in warm seawater and other high chloride environments. The high nickel content results in better resistance to stress corrosion than standard austenitic grades. Copper in the alloy adds resistance to sulfuric and other reducing acids particularly in the very aggressive “medium concentration” range. In most environments, AISI 904L UNS N08904 W 1.4539 steel has intermediate corrosion performance between the standard 316L austenitic grade and types of molybdenum-rich (about 6%) or super austenitic materials.
AISI 904L steel UNS N08904 W 1.4539 should not be used at temperatures above about 550°C.
It finds application in piping systems pollution control equipment heat exchangers and bleaching systems.
CHEMICAL COMPOSITION AISI 904L UNS N08904 W 1.4539
| Element | Min | Max |
|---|---|---|
| C | 0.02 | |
| S | 0.035 | |
| P | 0.045 | |
| Yes | 1.00 | |
| Mn | 2.00 | |
| Cr | 19.00 | 23.00 |
| Ni | 23.00 | 28.00 |
| Mo | 4.00 | 5.00 |
| Cu | 1.00 | 2.00 |
MECHANICAL CHARACTERISTICS AISI 904L UNS N08904 W 1.4539
| Material | League | Rm min (MPa) | Rp 0.2 min (MPa) | A% min | Hardness min |
|---|---|---|---|---|---|
| AISI 904L UNS N08904 | 1.4539 | 530 | 230 | 35 | 230 |
PHYSICAL PROPERTIES AISI 904L UNS N08904 W 1.4539
- Specific gravity: kg/cm3 20°C – 80 kg/dm3
- Modulus of elasticity: N/mm2 20°C – 195,000
- Thermal conductivity: W/m.K. (20°C) – 12
- Specific heat: J/g.K. (20°C) – 450
- Coefficients of linear expansion: 20° – 200°C – 161, 20° – 400°C – 169, 20° – 600°C – 175
- Electrical resistivity: Ω mm2/m 20°C 100
- Amagnetic
SPECIFICATIONS AND DESIGNATIONS
- W.: 1.4539
- UNS: UNS N08904
- Swedish: 2526
- Brand: URANUS® B6
- AISI: 904L