1.4923 X22CrMoV12-1
Steel 1.4923 X22CrMoV12-1 is a high-strength quenching steel suitable for high temperature applications that is not corrosion resistant. It falls within the range of materials suitable for the production of fasteners for applications involving -200° to +700°C defined by ISO 267-13 and ISO EN 10269. Steel 1.4923 X22CrMoV12-1 is particularly used for applications up to a maximum of 500°C obviously with a considerable drop in mechanical properties (at 500°C Rm = 335 MPa). This alloy is especially used for endothermic engine parts, pumps, piping and valves.
CHEMICAL COMPOSITION 1.4923 X22CrMoV12-1
| Element | Min | Max |
|---|---|---|
| C | 0.18 | 0.24 |
| Yes | 0.40 | 0.50 |
| Mn | — | 0.90 |
| P | — | 0.025 |
| S | — | 0.015 |
| Cr | 11.00 | 12.50 |
| Mo | 0.80 | 1.20 |
| Ni | 0.30 | 0.80 |
| V | 0.25 | 0.35 |
MECHANICAL PROPERTIES 1.4923 X22CrMoV12-1
| Material | League | Rm (MPa) | Rp 0.2 min (MPa) | A% min | Z% min | Hardness | Impact test min (KV2) (J) |
|---|---|---|---|---|---|---|---|
| 1.4923 X22CrMoV12-1 + QT1 | 1.4923 | 800 – 950 | 650 | 14 | 40 | 22 – 29 HRC | 27J at 20°C |
| 1.4923 X22CrMoV12-1 + QT2 | 1.4923 | 900 – 1050 | 750 | 11 | 35 | 26 – 33 HRC | 20J at 20°C |
PHYSICAL PROPERTIES 1.4923 X22CrMoV12-1
- Specific gravity at 20°C: 7.95 kg/dm³
- Modulus of elasticity at 20°C: 199,000 N/mm²
CORRESPONDENCE AND SPECIFICATIONS 1.4923 X22CrMoV12-1
- W.: 1.4923
- EN: 10269
- ISO: 267-13
- DIN: 2510
- DIN EN ISO: 898
- ISO: 3506